RheTech Products F38-01 35% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products F38-01 35% Glass Fiber/Mineral Co-Reinforced Polypropylene, Chemically Coupled, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical housingsBracketsBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 35 % | 35 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0026 cm/cm | 0.0026 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 77 | 77 | ASTM D2240 |
| Tensile Strength at Break | 53.8 MPa | 7800 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 4.83 GPa | 700 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Temperature 23.0 °C |
0.900 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.339 J | 0.250 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 310 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Kostat 7440 Conductive ABS Compound
- Lubriplate 1242 Lithium-Polymer Type Multi-Purpose Grease
- Solvay Specialty Polymers Torlon® 4000T Polyamide-imide (PAI)
- Teknor Apex Sinvicomp SMG 3500 Polyvinyl Chloride, Flexible
- Total PPH 3480Z Polypropylene, Extrusion Grade
- CIMBAR Gel Talc for Polyester Filler
- Clariant PA612G30 Nylon 612, 30% Glass Fiber, Impact Modified
- 3M Scotchcal™ ElectroCut™ 7125-103 Graphic Film
- BASF Lupranate® 5220 Isocyanate
- SABIC Innovative Plastics ULTEM 1010M PEI
Copyright © lookpolymers.com All Rights Reserved