Multibase Multi-Pro® 4006 TH Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Multibase
Trade Name Multi-Pro®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Pro® 4006 TH Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Talc Filled, 40% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: ConnectorsElectrical/Electronic ApplicationsAppliancesInformation provided by Multibase
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0080 cm/cm
0.0080 in/in
ASTM D955
Melt Flow 6.0 g/10 min
6.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 30.3 MPa
4400 psi
ASTM D638
Elongation at Break 25 %
25 %
ASTM D638
Flexural Modulus 3.28 GPa
475 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm
0.600 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
245 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 221 °C
390 - 430 °F
Middle Barrel Temperature 204 - 232 °C
400 - 450 °F
Front Barrel Temperature 204 - 232 °C
400 - 450 °F
Nozzle Temperature 193 - 227 °C
380 - 440 °F
Mold Temperature 4.44 - 65.6 °C
40.0 - 150 °F
Drying Temperature 93.3 °C
200 °F
Dry Time 2 hour
2 hour
Back Pressure 0.138 - 0.345 MPa
20.0 - 50.0 psi
Screw Speed 40 - 100 rpm
40 - 100 rpm
Descriptive Properties Value Comments
Clamp Tonnage 2-4 tons/in2
Screw L/D Ratio 20:1