Ravago Manufacturing Americas Hylon® N1000EL Nylon 6/6 (Cond) (discontinued **)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1000EL Nylon 6/6 (Cond)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Strength | 40.7 MPa | 5900 psi | ASTM D790 |
| Flexural Modulus | 1.31 GPa | 190 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | 0.0590 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.0 @Frequency 100 Hz |
6.0 @Frequency 100 Hz |
ASTM D150 |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 140 rpm | 40 - 140 rpm |
Users viewing this material also viewed the following:
- Kazanorgsintez Diethanolamine, Technical
- Fine Organics FINALUX CL 5 Composite Lubricant
- LG Chemical KEYFLEX BT 10288D Ester Type TPE
- Ineos N01G-02 Polypropylene Impact Copolymer
- Sharadaa Ceramics ZAP 007 Smart Cast Application
- Borealis FT3200 Low Density Polyethylene
- Eagle Brass 770 Nickel Silver 18%, Hard
- Crucible Steel SIL10 Martensitic Steel
- ACC EP JS EPI Engineered Polymers Joint Sealant
Copyright © lookpolymers.com All Rights Reserved