LG Chemical Lupox® NH2306F PBT+GF30%

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name Lupox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical Lupox® NH2306F PBT+GF30%.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PBT+GF30%, Halogen Free Flame RetardantApplication: IT/OA, E&E (Connector)CAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.57 g/cc
1.57 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0030 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 98.1 MPa

@Thickness 3.20 mm
 14200 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 150 MPa

@Thickness 3.20 mm
 21800 psi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Flexural Modulus 8.34 GPa

@Thickness 3.20 mm
 1210 ksi

@Thickness 0.126 in
 1.3mm/min; ASTM D790
Izod Impact, Notched 0.588 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 1.10 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
@ Break; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C

@Thickness 6.40 mm
 419 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 75.0 °C

@Thickness >=0.800 mm
 167 °F

@Thickness >=0.0315 in
75.0 °C

@Thickness >=1.60 mm
 167 °F

@Thickness >=0.0630 in
75.0 °C

@Thickness >=3.20 mm
 167 °F

@Thickness >=0.126 in
UL RTI, Mechanical with Impact 75.0 °C

@Thickness >=0.800 mm
 167 °F

@Thickness >=0.0315 in
75.0 °C

@Thickness >=1.60 mm
 167 °F

@Thickness >=0.0630 in
75.0 °C

@Thickness >=3.20 mm
 167 °F

@Thickness >=0.126 in
UL RTI, Mechanical without Impact 75.0 °C

@Thickness >=0.800 mm
 167 °F

@Thickness >=0.0315 in
75.0 °C

@Thickness >=1.60 mm
 167 °F

@Thickness >=0.0630 in
75.0 °C

@Thickness >=3.20 mm
 167 °F

@Thickness >=0.126 in
Flammability, UL94 V-0

@Thickness >=0.800 mm
 V-0

@Thickness >=0.0315 in
V-0

@Thickness >=1.60 mm
 V-0

@Thickness >=0.0630 in
V-0

@Thickness >=3.20 mm
 V-0

@Thickness >=0.126 in
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 60 - 120 sec

@Thickness >=0.800 mm
 60 - 120 sec

@Thickness >=0.0315 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.800 mm
 >= 120 arcs

@Thickness 0.0315 in
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 250 °C
455 - 482 °F
Injection Molding
Middle Barrel Temperature 240 - 250 °C
464 - 482 °F
Injection Molding
Front Barrel Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Nozzle Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Melt Temperature 245 - 255 °C
473 - 491 °F
Injection Molding
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Injection Molding
Drying Temperature 120 °C
248 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding