- Polymer Resources PC-GP4-[color]-3 Polycarbonate, UV-stabilized, Easy Flow
Polymer Resources PC-GP4-[color]-3 Polycarbonate, UV-stabilized, Easy Flow
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC-GP4-[color]-3 Polycarbonate, UV-stabilized, Easy Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, UV-stabilized, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Flexural Strength | 92.4 MPa | 13400 psi | ASTM D790 |
| Flexural Modulus | 2.28 GPa | 330 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Temperature 22.8 °C |
12.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.70 mm |
V-2 @Thickness 0.0669 in |
|
| V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Front Barrel Temperature | 271 - 293 °C | 520 - 560 °F | |
| Melt Temperature | 266 - 293 °C | 510 - 560 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 118 - 124 °C | 245 - 255 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- RheTech Products FT4200-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural
- Outokumpu 2205 Duplex Stainless Steel
- Garlock 2930 Compressed Aramid Fiber Gasketing, Neoprene Binder
- Minelco Q-Lite 70 Mullite Chamotte
- Ineos ABS Lustran® ABS E112LG Pellets
- Solvay Specialty Polymers Amodel® AS-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned)
- Ter Hell Plastic Terez® PA 6 7751 TGF 15 GL Polyamide 6, 15% Glass Fiber
- Hexcel® HexForce™ 4527 Fiber Glass Fabric
- Trelleborg AEM Eccospheres® SI-350 Sodium Borosilicate Glass Microspheres
- Dow Corning 236 DISPERSION
Copyright © lookpolymers.com All Rights Reserved