- Styron CALIBREâ„¢ 200-10 Polycarbonate Resin
Styron CALIBREâ„¢ 200-10 Polycarbonate Resin
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | CALIBRE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron CALIBREâ„¢ 200-10 Polycarbonate Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Overview: CALIBREâ„¢ 200-10 Series are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity. The CALIBREâ„¢ 200-10 series products are available in 2 additive packages: CALIBREâ„¢ 200: No mold release or UV Stabilizer. CALIBREâ„¢ 201: Mold release. Applications:Food and processor housingsLiquid containersFood utensilsPackaging applicationsGovt. and Industry Standards:US FDA 21 CFR 177.1580Underwriters Laboratory (UL)EU food contact 2002/72/ECInformation provided by Styron
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | ISO 527-2/50 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-2/50 |
| Elongation at Break | 150 % | 150 % | ISO 527-2/50 |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-2/50 |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO 527-2/50 |
| Flexural Strength | 97.0 MPa | 14100 psi | 2.0 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2.0 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 88.0 kJ/m² @Temperature 23.0 °C |
41.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 125 °C | 257 °F | IEC 60335-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 °C | 291 °F | Annealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Unannealed; ISO 75-2/A |
| 141 °C | 286 °F | Annealed; ISO 75-2/A | |
| Vicat Softening Point | 149 °C | 300 °F | ISO 306/B50 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 87 - 91 % | 87 - 91 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 V @Thickness 2.00 mm |
250 V @Thickness 0.0787 in |
IEC 60112 |
Users viewing this material also viewed the following:
- Plaskolite Optix® Acrylic Sheet
- Nye Lubricants 825F-1 (FG) Synthetic Oil
- Nylene® 615SA Nylon 6, Film Grade
- Premix Thermoplastics PRE-ELEC® ESD 5500 Static Dissipative Thermoplastic Compound
- Ineos ABS Triax® DP 3155 ABS + Polyamide Blend (DAM) (discontinued **)
- Lanxess Durethan® AKV 35 H2.0 SR1 901510 Nylon 66, Glass Fiber Reinforced
- Solvay Specialty Polymers Halar® 1450LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Styrolution NOVODUR® P2HGV ABS, 16% Glass Fiber
- Hippe PBT Polybutylene Terephthalate
- Dow LDPE 752A Low Density Polyethylene, Film Grade
Copyright © lookpolymers.com All Rights Reserved