- Polykemi AB POLYblend 65H PC/ABS-Blend
Polykemi AB POLYblend 65H PC/ABS-Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYblend |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Polykemi AB POLYblend 65H PC/ABS-Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | With Flow; ISO 2577 |
| 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 15 g/10 min <br>@Load 5.00 kg,<br> Temperature 260 °C |
15 g/10 min <br>@Load 11.0 lb,<br> Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Elongation at Yield | 5.0 % | 5.0 % | ISO/R527 |
| Flexural Strength | <= 95.0 MPa | <= 13800 psi | ISO 178 |
| Flexural Modulus | 2.30 GPa <br>@Temperature 23.0 °C |
334 ksi <br>@Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 2.50 J/cm² <br>@Temperature -20.0 °C |
11.9 ft-lb/in² <br>@Temperature -4.00 °F |
ISO 179 |
| 4.00 J/cm² <br>@Temperature 23.0 °C |
19.0 ft-lb/in² <br>@Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 120 °C <br>@Load 5.001 kg |
248 °F <br>@Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C <br>@Thickness 2.00 mm |
1200 °F <br>@Thickness 0.0787 in |
IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 2 - 8 hour | 2 - 8 hour | in circulation dryer |
| 2 - 8 hour | 2 - 8 hour | in fresh-air dryer | |
| 2 - 8 hour | 2 - 8 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-50 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Rotuba 860S Ethyl Cellulose
- Heraeus Cleviosâ„¢ P Jet N V2 Conductive Sulfonate Polymer for Antistatic Coatings
- Techmer ES HiFill® HDPE TM30 30% Talc Filled
- UCAR Carbon UCAR® ATA Isostatic Molded Graphite
- Toyobo Pelprene™ S-6001 Polyester TPE
- 3M 12062 Black 3/32" (2.4 mm) Polyurethane Foam
- Braskem Flexus® 7200 LLDPE Cast Film Extrusion
- Akzo Nobel Expancel® 091 WUF 40 Wet unexpanded microspheres
- Qualchem Danamid FGFL0-20 Polyamide 6, 20% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved