Plastcom PLASTALEN® PQ 83 T 30 Polypropylene reinforced with mineral filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Plastcom spol. s r.o.
Trade Name PLASTALEN®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom PLASTALEN® PQ 83 T 30 Polypropylene reinforced with mineral filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Impact modified PP for injection molding with the content of 30 % mineral filler. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
STN EN ISO 1183-1
Filler Content 30 %
30 %
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
STN EN ISO 294-4
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
STN EN ISO 294-4
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 13.0 MPa
1890 psi
STN EN ISO 527-2
Elongation at Break 3.0 %
3.0 %
STN EN ISO 527-2
Tensile Modulus 1.50 GPa
218 ksi
STN EN ISO 527-2
Flexural Strength 20.0 MPa
2900 psi
STN EN ISO 178
Flexural Modulus 1.25 GPa
181 ksi
STN EN ISO 178
Charpy Impact Unnotched 2.20 J/cm²

@Temperature -20.0 °C
10.5 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Charpy Impact, Notched 0.350 J/cm²

@Temperature -20.0 °C
1.67 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
1.80 J/cm²

@Temperature 23.0 °C
8.57 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
STN EN 11357-1
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C
162 °F
STN EN ISO 75-2 (A)
Vicat Softening Point 117 °C
243 °F
STN EN ISO 306
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Moisture Content 0.10 %
0.10 %
STN EN ISO 3344
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi
Descriptive Properties Value Comments
Color Black