LG Chemical MA201 ABS, Low Gloss

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical MA201 ABS, Low Gloss.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, Extrusion Molding, General Purpose, Low GlossApplication: Automotive Sheet, Semi-Conductor TrayCAS No. 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Water Absorption 0.19 %

@Temperature 23.0 °C,
Time 86400 sec
0.19 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Maximum Moisture Content 0.010
0.010
Injection and Extrusion Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 51.0 MPa

@Thickness 3.20 mm
7400 psi

@Thickness 0.126 in
50 mm/min; ASTM D638
Elongation at Break >= 30 %

@Thickness 3.20 mm
>= 30 %

@Thickness 0.126 in
50 mm/min; ASTM D638
Flexural Yield Strength 73.5 MPa

@Thickness 3.20 mm
10700 psi

@Thickness 0.126 in
15 mm/min; ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.20 mm
370 ksi

@Thickness 0.126 in
15 mm/min; ASTM D790
Izod Impact, Notched 2.55 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
4.78 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D256
3.92 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
7.35 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched 1.08 J/cm

@Thickness 6.40 mm,
Temperature -20.0 °C
2.02 ft-lb/in

@Thickness 0.252 in,
Temperature -4.00 °F
ASTM D256
1.86 J/cm

@Thickness 3.20 mm,
Temperature -20.0 °C
3.49 ft-lb/in

@Thickness 0.126 in,
Temperature -4.00 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C

@Thickness 6.40 mm
198 °F

@Thickness 0.252 in
Unannealed; ASTM D648
Vicat Softening Point 100 °C

@Load 5.00 kg
212 °F

@Load 11.0 lb
50°C/h; ASTM D1525
Flammability, UL94 HB

@Thickness >=0.800 mm
HB

@Thickness >=0.0315 in
HB

@Thickness >=1.60 mm
HB

@Thickness >=0.0630 in
HB

@Thickness >=2.50 mm
HB

@Thickness >=0.0984 in
HB

@Thickness >=3.20 mm
HB

@Thickness >=0.126 in
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Zone 1 180 - 200 °C
356 - 392 °F
Extrusion Molding
Zone 2 190 - 210 °C
374 - 410 °F
Extrusion Molding
Zone 3 200 - 230 °C
392 - 446 °F
Extrusion Molding
Zone 4 200 - 230 °C
392 - 446 °F
Extrusion Molding
Adapter Temperature 200 - 230 °C
392 - 446 °F
Extrusion Molding
Die Temperature 200 - 230 °C
392 - 446 °F
Extrusion Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection and Extrusion Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Roll Temperature 60.0 - 90.0 °C
140 - 194 °F
Bottom, Extrusion
70.0 - 90.0 °C
158 - 194 °F
Middle, Extrusion
70.0 - 100 °C
158 - 212 °F
Top, Extrusion
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection and Extrusion Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection and Extrusion Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding