- Nilit FRIANYL A63 TF20 Nylon 6.6 for injection molding, 20% PTFE lubricated
Nilit FRIANYL A63 TF20 Nylon 6.6 for injection molding, 20% PTFE lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, PTFE Filled |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 TF20 Nylon 6.6 for injection molding, 20% PTFE lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 - 1.0 % | 0.90 - 1.0 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.014 - 0.020 cm/cm | 0.014 - 0.020 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 50.0 MPa | 7250 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 4.00 J/cm² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 1.00 J/cm² | 4.76 ft-lb/in² | DIN 53453 | |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |
| 0.800 J/cm² @Temperature -40.0 °C |
3.81 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Braskem HB 0055 HDPE Blow Molding Polyethylene (discontinued **)
- Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (Conditioned)
- Lubriplate 630-AAA Lithium Based Multi-Purpose Grease
- SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE
- ELASTO UK Dryflex® 662600S SEBS Based Material, Semi-Filled Qualities, 60A Hardness, Black
- Alliance N-35 Neodymium Iron Boron Magnetic Material
- Parker Chomerics POLASHEET® Metal EMI Gasket
- Fainplast Compounds MPH 85 Medical Flexible PVC, Extrusion
- ExxonMobil Escorene® LD-713 High EVA Film Resin (discontinued **)
- Zircar Zirconia ZHB Zirconia Hollow Balls
Copyright © lookpolymers.com All Rights Reserved