Multibase Multi-Pro® 5014 CUW Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 5014 CUW Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Calcium Carbonate Filler. Forms:PelletsProcessing Methods:Injection MoldingUses:FurnitureInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.5 MPa | 3850 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Flexural Yield Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 8.248 J | 6.083 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
Users viewing this material also viewed the following:
- PolyOne Geon™ CPVC MC500 Polyvinyl Chloride, Chlorinated (CPVC)
- Star Plastics PC733R Molding Grade PC
- Teknor Apex APEX® 80862-F Polyvinyl Chloride, Flexible
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- Eagle Brass 110 EPT COPPER, 1/4 Hard
- DSM Akulon® S223-HPG5 Impact Modified Nylon 66-25% Glass Reinforced (European Grade) (Cond)
- ChevronTexaco Rykon® 1426 Premium Grease
- Dow LDPE 4005 Low Density Polyethylene, Extrusion Coating Grade
- 3M Dyneon™ FC 2181 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved