SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X10401H ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.260 % | 0.260 % | 50% RH, 24 hrs; ASTM D570 |
| 0.470 % | 0.470 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 12 % | 12 % | Type I, 5 mm/min; ASTM D638 |
| 12 % | 12 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.55 GPa | 370 ksi | 1 mm/min; ISO 527 |
| 2.66 GPa | 386 ksi | 5 mm/min; ASTM D638 | |
| Flexural Modulus | 2.57 GPa | 373 ksi | 2 mm/min; ISO 178 |
| 2.72 GPa | 395 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.860 J/cm | 1.61 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.4 J/cm | 30.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 175 kJ/m² | 83.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 34.0 J @Temperature 23.0 °C |
25.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 29.0 J | 21.4 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
29.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 214 °C @Thickness 3.20 mm |
417 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Dow Questra® EA514 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **)
- Techmer ES Luriblend® PA6/6 GF15 ML3 15% Glass Filled
- Teknor Apex APEX® 84129 Polyvinyl Chloride, Flexible
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 50 PHR N990 (MT) Filler
- Teknor Apex Telcar® TL-2454A Thermoplastic Elastomer
- A. Schulman POLYTROPE™ TPP 510 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Eastman Eastman F-Cat HC Polyester Concentrate
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 427°C Temper
- ATI Allegheny Ludlum Stainless Steel Type 201L, Annealed (UNS S20103)
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved