Isoflon PVDF Polyvinylidene fluoride
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PVDF Polyvinylidene fluoride.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Electrical and thermal insulating products with food slipping propertiesChemically inertInformation provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 g/cc | 1.75 g/cc | DIN 53479 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength | 45.0 MPa | 6530 psi | DIN 53455 |
| Elongation at Break | 150 % | 150 % | DIN 53455 |
| Tensile Modulus | 1.70 GPa | 247 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 165 - 178 °C | 329 - 352 °F | DIN 53736 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | Continuous; DIN 52612 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | DIN 53482 |
| Dielectric Constant | 7.8 @Frequency 1000 Hz |
7.8 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 18.0 - 50.0 kV/mm | 457 - 1270 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Opaque |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Algoflon® S 131 PTFE (Polytetrafluoroethylene) (discontinued **)
- Huntsman Araldite GT 6609 US Bisphenol A Epoxy Solid Resin
- LG Chemical SEETEC M1400 Polypropylene Impact Copolymer
- Johnson Matthey LM 5 Soft Solder/Flux
- Lubrizol STAT-RITE® S-1100 Static Dissipative TPU
- A. Schulman POLYBATCH™ Blue Tint P40530 Concentrate Based In Homopolymer Polypropylene
- BASF Formic Acid - 99-100%
- Arlon 56096R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Bulk Molding Compounds BMC T12-15526 General Purpose Molding Compound
Copyright © lookpolymers.com All Rights Reserved