- Multibase Multi-Pro® 4015 THW Polypropylene
Multibase Multi-Pro® 4015 THW Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 4015 THW Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Talc Filled, 40% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: Lawn and Garden EquipmentTable ProductsFurnitureInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Modulus | 3.24 GPa | 470 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 221 °C | 390 - 430 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- MV Labs ZN100 Zn(OAC)2·xH2O Zinc acetate hydrate
- Huntsman PE 1017 Film Extrusion Polyethylene (discontinued **)
- Lubriplate SYNXTREME FG-2 Calcium Sulfonate Complex Synthetic Food Machinery Grade Grease
- Samsung Cheil Industries Infino® GP-5000 PBT, Unreinforced
- Styron MAGNUMâ„¢ 8391 Acrylonitrile Butadiene Styrene (ABS) Resin
- Teknor Apex Monprene® MP-1870-CR Thermoplastic Elastomer
- Aclo Accutech Polypropylene Copolymer CP0436C30L1 Calcium Reinforced
Copyright © lookpolymers.com All Rights Reserved