Multibase Multi-Pro® 2006 T Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 2006 T Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Talc Filler, 20% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.1 MPa | 4510 psi | ASTM D638 |
| Elongation at Break | 62 % | 62 % | ASTM D638 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm | 0.700 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 221 °C | 390 - 430 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 2-4 tons/in2 | |
| Screw L/D Ratio | 20:1 |
Users viewing this material also viewed the following:
- Solvay Engineered Polymers SEQUEL® 1402 TPO (discontinued **)
- Karina E 701D02/128-SD Yellow PVC Compound
- LG Chemical LUPOL LW4405 PP+GF/MF40%
- SABIC Innovative Plastics LNP Stat-kon KS302 Acetal Copoly
- Samsung Cheil Industries Starex® CM-0140UV ABS, Unreinforced
- A. Schulman ComAlloy® E-17036 Glass Fiber Reinforced High Heat Polycarbonate
- Cresset Powers Cress-Alon™ NF3020 2% Nano Clay Loaded, 3.0 r.v. Film Grade Nylon 6, Dry As Molded
- BASF Ultramid® SEGM35 H1 BK-126 15/25% Glass/Mineral Filled PA6 (Dry)
- BASF TEHA Tris-(2-ethylhexyl)amine
Copyright © lookpolymers.com All Rights Reserved