Plastics Group Polifil® RMT-40V 40% Talc-Reinforced Polypropylene, High Impact, UV Stabilized

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer The Plastics Group of America
Trade Name Polifil®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastics Group Polifil® RMT-40V 40% Talc-Reinforced Polypropylene, High Impact, UV Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polifil® RMT-V series compounds are high impact, UV stabilized polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and the ability to retain their original color and state.Applications: Outdoor furnitureAutomotiveAppliancesStandard processing techniques are applicable. Information provided by The Plastics Group.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
Filler Content 40 %
40 %
ASTM D2584
Linear Mold Shrinkage 0.010 cm/cm

@Thickness 1.59 mm
0.010 in/in

@Thickness 0.0625 in
ASTM D955
Melt Flow 16 - 20 g/10 min
16 - 20 g/10 min
230/2.16; May be specified; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 88
88
ASTM D785
Tensile Strength at Break 25.9 MPa
3750 psi
ASTM D638
Flexural Modulus 2.76 GPa
400 ksi
Tangent; ASTM D790
Izod Impact, Notched 0.641 J/cm
1.20 ft-lb/in
At 73°F; ASTM D256
Izod Impact, Unnotched 3.47 J/cm
6.50 ft-lb/in
At 73°F; ASTM D256
Gardner Impact 4.519 J
3.333 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 127 °C
260 °F
ASTM D648