Lehmann & Voss LUVOCOM® 19-7969 Polyamide 46, with aramid reinforcement and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19-7969 Polyamide 46, with aramid reinforcement and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Good friction and wear behaviour especially at increased temperatures.Emergency running property.Bearings, sleeves, sliding elements, control disks, gear wheels, duty parts in switches.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 85.0 MPa | 12300 psi | |
| Elongation at Yield | 6.5 % | 6.5 % | |
| 8.5 % | 8.5 % | flexural | |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | |
| Flexural Strength | 120 MPa | 17400 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Plenco 50240 PET, Pellet, Injection Molded, Natural Color (discontinued **)
- Overview of materials for PVC, Uncompounded
- LG Chemical LUMID LW4403B(W) PA66+GF/MF40%, Low Warpage
- Heraeus Cleviosâ„¢ P T2 Conductive Sulfonate Polymer for Antistatic Coatings
- A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene
- Corning Macor® Machinable Glass Ceramic
- Daikin NEOFLON AP-221SH PFA Semiconductor Grade
- Ametek High Purity Nickel Strip 899L 3/4 Hard
- Bulk Molding Compounds BMC T45HT Automotive Grade Molding compound
- Lucite International Diakon® Frost 902 80 Acrylic Polymer
Copyright © lookpolymers.com All Rights Reserved