Sibur ONZ-40 Compound M-258 Polyvinyl Chloride (PVC)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Sibur |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sibur ONZ-40 Compound M-258 Polyvinyl Chloride (PVC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. For insulation of wires and cables operating in intervals of temperatures from -40°C to 70°C.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 - 1.31 g/cc | 0.0452 - 0.0473 lb/in³ | |
| Water Absorption | <= 0.30 % | <= 0.30 % | |
| Collected Volatile Condensable Material | <= 3.0 % | <= 3.0 % | Loss in mass at 160°C during 6 hours |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 13.7 MPa | >= 1990 psi | |
| Elongation at Break | >= 300 % | >= 300 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Softening Point | 165 - 185 °C | 329 - 365 °F | |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | |
| Flammability Test | <= 30 | <= 30 | In seconds, method A |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 5.00e+11 ohm-cm @Temperature 20.0 °C |
>= 5.00e+11 ohm-cm @Temperature 68.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Non-colored, black | |
| Elongation Retained After Ageing | 80% | Aged for 7 days at 100±2°C |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 45 PA66, 45% glass fibre
- ExxonMobil LL 6235.19 Injection Molding Resin (discontinued **)
- Ineos ABS Lustran® M201AS
- ICE Al2O3 94
- Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F)
- A. Schulman POLYBATCH™ Orange LL10257/4 Concentrate Based In LLDPE
- Chi Mei Polylac® PA-716 ABS - High Flow
- Fainplast Compounds GS 78 Flexible PVC, Injection Molding for Technical Items
- Arlon Thermabond® 48991A010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Arkema Group LOTADER® 8200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
Copyright © lookpolymers.com All Rights Reserved