Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | FRISETTA Test Method |
Nilit FRIANYL B63 KV25 Nylon 6 for injection molding, 25% glass ball reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.012 - 0.018 cm/cm | 0.012 - 0.018 in/in | ASTM D955 |
Polymer Resources NY66-MD1 Nylon 66, 1% MoS2 Nylon 66, 1% Molybdenum Disulfide for Lubrication and WearProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon.. |
|||
Linear Mold Shrinkage | 0.013 - 0.018 cm/cm | 0.013 - 0.018 in/in | ASTM D955 |
Polymer Resources PC/TP-GP3-IM PC/Polyester Alloy, Impact Modified Superior Chemical Resistance, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provide.. |
|||
Linear Mold Shrinkage | 0.010 - 0.018 cm/cm | 0.010 - 0.018 in/in | ASTM D955 |
Alcoa KAMA 5100 CPET
(discontinued **) CapabilitiesGauge: .020" to .040" (508 to 106µm)Width: 20" to 52" (508 to 1321mm)Core size: 3" or 6"Roll O.D.: 29" standard, available up to 40"Silicone coating availableAvailable in natural blackP.. |
|||
Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | after bake; ISO 294 |
Solvay Engineered Polymers DEXFLEX® 810HS TPO
(discontinued **) Description: DEXFLEX® 810HS is a thermoplastic olefinic elastomer (TPO) that offers excellent weatherability, paintability and processability. This material is designed to exceed the requirements .. |
|||
Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYfill PPC 12000 Polypropylene Copolymer Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | With Flow; ISO 2577 |
Polykemi AB POLYfill PPC 20000 Polypropylene Copolymer Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.013 - 0.018 cm/cm | 0.013 - 0.018 in/in | ASTM D955 |
Polymer Resources PC/TP-GP3 PC/Polyester Alloy High Impact, Superior Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by.. |
|||
Linear Mold Shrinkage | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | FRISETTA Test Method |
Nilit FRIANYL B63 W-KV10 Nylon 6 for injection molding, 10% glass ball reinforced Nylon 6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.0090 - 0.018 cm/cm | 0.0090 - 0.018 in/in | |
Lehmann & Voss LUVOCOM® 1850-7692/BK PBT, with glass spheres and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteri.. |
|||
Linear Mold Shrinkage | 0.012 - 0.018 cm/cm @Thickness 1.60 mm |
0.012 - 0.018 in/in @Thickness 0.0630 in |
ASTM D955 |
Gromax PBT 1100-211S Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Linear Mold Shrinkage | 0.012 - 0.018 cm/cm @Thickness 1.60 mm |
0.012 - 0.018 in/in @Thickness 0.0630 in |
ASTM D955 |
Gromax CCP PBT 1100-104S Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce.. |
|||
Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
Polyram PlusTek PA340S05 Nylon 6.6 for Injection Molding, 5% Glass-beads Reinforced, Heat Stabilized 5% Glass-beads reinforced Nylon 6.6, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | |
Polyram PlusTek PA602 Nylon 6.6, Heat Stabilized Heat stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
Polyram PlusTek PA700BL10 Nylon 6.6 for Injection Molding, UV Stabilized UV Stabilized Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
Polyram PlusTek PA801 Nylon 6.6 Copolymer for Injection Molding, Impact Modified Impact modified Nylon 6.6 copolymer for injection molding application.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 2577 |
Polyram PlusTek PA804 Nylon 6.6 for Injection Molding, Impact Modified Impact modified Nylon 6.6 for injection molding application.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.0060 - 0.018 cm/cm @Thickness 3.20 mm |
0.0060 - 0.018 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer DescriptionFormion® FI 105 is a non-reinforced, transparent, injection molding grade Sodium Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and .. |
|||
Linear Mold Shrinkage | 0.0060 - 0.018 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0060 - 0.018 in/in @Thickness 0.126 in, Time 72.0 hour |
ISO 294 |
A. Schulman FORMION™ FI 120 Non-Reinforced, Injection Molding Grade Zinc Ionomer DescriptionFormion® FI 120 is a non-reinforced, transparent, injection molding grade Zinc Ionomer. It has been formulated for high durability, scratch resistance, low temperature ductility, and lo.. |
|||
Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in | after bake; ISO 294 |
Solvay Engineered Polymers DEXFLEX® 826HS TPO
(discontinued **) Description: DEXFLEX® 826HS is a thermoplastic olefinic elastomer (TPO) designed for automotive exterior applications that require a combination of stiffness, low-temperature impact resistance, and.. |
|||
Linear Mold Shrinkage | 0.013 - 0.018 cm/cm | 0.013 - 0.018 in/in | ASTM D955 |
Polymer Resources PC/TP-GP3 PC Polyester, High Impact, Superior Chemical Resistance
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |