Aardvark Polymers AARTEL® 800 Rotational Molding Resin
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | Gehrig & Associates |
| Trade Name | AARTEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aardvark Polymers AARTEL® 800 Rotational Molding Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aartel 800 is our high test, general purpose, acetal copolymer. Aartel 800 provides overall excellent performance for most applications and is available in natural (off white) and a wide range of standard colors.Information provided by Gehrig & Associates
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | ISO 294-4 |
| Melt Flow | 11.28 g/10 min @Load 2.16 kg, Temperature 190 °C |
11.28 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | (50mm/min); ISO 527-2/1A |
| Elongation at Yield | 9.7 % | 9.7 % | (50mm/min); ISO 527-2/1A |
| Tensile Modulus | 2.76 GPa | 400 ksi | (1mm/min); ISO 527-2/1A |
| Flexural Modulus | 2.55 GPa | 370 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.70 kJ/m² @Temperature 23.0 °C |
2.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 18.1 J/cm² @Temperature -30.0 °C |
86.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1e |
| 18.8 J/cm² @Temperature 23.0 °C |
89.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1e | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1e |
| 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1e |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | (10°C/min); ISO 11357-1,2,3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75-1/-2 |
Users viewing this material also viewed the following:
- Custom Resins Vexel™ E20GF30 , 30% Glass Reinforced PET (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000EHL Nylon 6/6 (Cond) (discontinued **)
- Materion BrushCAST® 21C High Strength Casting Alloy (As Cast)
- Lucent Polymers GPP-320 Polypropylene, 20% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- A. Schulman POLYBATCH™ Yellow 26787V Concentrate Based In LDPE
- Polyram RamSter RF303G6 PBT, 30% Glass Fiber, Industrial Grade
- Dow SE SLR-6410 Solution polymerized Styrene Butadiene Rubber (S-SBR)
- ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 1149°C (2100°F) + Age
- Bhansali Engineering Abstron AN480V2 Flame Retardant ABS Grade
Copyright © lookpolymers.com All Rights Reserved