Lanxess Durethan® TP 142-011 900116 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® TP 142-011 900116 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 9.8 % | 9.8 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.013 cm/cm | 0.013 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.015 cm/cm | 0.015 in/in | 60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | d.a.m.; ISO 527-1, -2; 50 mm/min |
| Elongation at Break | 110 % | 110 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| Elongation at Yield | 3.8 % | 3.8 % | d.a.m.; ISO 527-1, -2; 50 mm/min |
| Tensile Modulus | 0.470 GPa | 68.2 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 2.00 GPa | 290 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 20.0 MPa @Strain 9.50 % |
2900 psi @Strain 9.50 % |
cond., 2 mm/min; ISO 178-A |
| 70.0 MPa @Strain 6.00 % |
10200 psi @Strain 6.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 14.0 MPa @Strain 3.50 % |
2030 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 60.0 MPa @Strain 3.50 % |
8700 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 0.470 GPa | 68.2 ksi | cond., 2 mm/min; ISO 178-A |
| 1.80 GPa | 261 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 100 kJ/m² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C |
9.52 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 13.0 J/cm² @Temperature 23.0 °C |
61.9 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA | |
| Puncture Energy | 64.0 J @Load <=510 kg, Temperature 23.0 °C |
47.2 ft-lb @Load <=1120 lb, Temperature 73.4 °F |
ISO 6603-2 |
| 64.0 J @Load <=5810 kg, Temperature -30.0 °C |
47.2 ft-lb @Load <=12800 lb, Temperature -22.0 °F |
ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 150 µm/m-°C @Temperature 23.0 - 55.0 °C |
83.3 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C @Temperature 23.0 - 55.0 °C |
83.3 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 280 °C | 446 - 536 °F | |
| 260 °C | 500 °F | for test specimens; ISO 294 | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| 80.0 °C | 176 °F | for test specimens; ISO 294 | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.00 - 0.060 % | 0.00 - 0.060 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI, BHR, 14-020 |
Users viewing this material also viewed the following:
- NanoAmor 50% DWNT Double Walled Carbon Nanotubes
- SABIC Innovative Plastics Cycolac® G366 ABS (Europe-Africa-Middle East)
- Global HI-830 High Impact Polystyrene
- Greene Tweed CHEMRAZ® 605 Perfluoroelastomer
- Kingfa FRHIPS-8002 Flame Retardant Polystyrene
- Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber
- Seals Eastern 5053 Ethylene-Propylene Rubber
- Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix
- 3M FM052 Indoor UL Recognized Brite Silver Polyester Label Products
- BASF Ultramid® 1000-11 NF2001 PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved