Polymer Property : Flexural Modulus = 261 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.80 GPa	261 ksi
Plastcom SLOVALEN PC 51 C 20 PP, 20% mineral filling FeaturesModified homopolymer and copolymer PP for injection moulding with the contenct of 20% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Polycasa XT 610 PMMA QUINN XT sheets have good optical properties and a brilliant surface. QUINN XT sheets offer excellent transparency, good mechanical properties, are UV resistant, have very good weathering and ageing..
Flexural Modulus	1.80 GPa	261 ksi	1.3 mm/min, 50 mm span; ASTM D790
Ovation Polymers Opnyl OP66UT119 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All..
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYblend 6005B PC/ABS-Blend Information provided by Polykemi AB
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Premix Thermoplastics PRE-ELEC® PP 1393 Conductive Thermoplastic Compound PRE-ELEC® PP 1393 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a very low electrical resistivity,..
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PP CIP6015F Polypropylene, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB SCANFILL BOTTLE BY45C2 Blow Molding Grade Information provided by Polykemi AB
Flexural Modulus	1.80 - 10.3 GPa	261 - 1500 ksi	Average value: 6.16 GPa Grade Count:86
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu..
Flexural Modulus	1.80 GPa	261 ksi
Lehmann & Voss LUVOCOMÂ® 50/TF/15/GY04 Polycarbonate, with PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper..
Flexural Modulus	1.80 GPa	261 ksi
Lehmann & Voss LUVOCOMÂ® 80-8444 Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.dynamic stressReduced moment of inertia compared with metal parts.Isotropic shrinkage character..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Inno-Comp INNOPOLÂ® CS 2-7120 20% Talc Filled Polypropylene Copolymer INNOPOLÂ® CS 2-7120 is a 20 % talc-filled polypropylene block-copolymer compound /PP-B TD20 (ISO 1043)/. This grade is available in natural and custom colored form.INNOPOLÂ® CS 2-7120 is recomme..
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
Inno-Comp INNOPOLÂ® CS 2-9523 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOLÂ® CS 2-9523 is a 20% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-9523 is dev..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Kuraray Genestarâ„¢ N1001D-U03 Nylon Standard unreinforced extrusion grade. Main Features:Outstanding fuel barrierHeat resistanceExample of applications:Multi-layered fuel tube
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Europe-Africa-Middle East) LNP* Stat-loy* A3000 is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat.
Flexural Modulus	1.80 GPa	261 ksi	ISO Data
Styrolution TerblendÂ® N NM-19 ABS/PA6 (Dry) Terblend N NM-19 is a UV stabilized ABS/PA6 blend combining very high impact strength, even at low temperatures with an excellent processability and surface appearance.Information provided by STYROL..
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX964 PPE+PA (Europe-Africa-Middle East) NORYL GTX964 is an unfilled impact modified material with optimised processability.
Flexural Modulus	1.80 GPa	261 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY P3000U PA 6 (Europe-Africa-Middle East) LNP* Stat-loy* P3000U is a compound based on PA 6 resin. Added features include; Antistatic, UV - Stabilized.
Flexural Modulus	1.80 GPa	261 ksi	Tangent; ISO 178
A. Schulman FORMION™ FI 232 10% Mineral Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 232 is an injection molding grade, 10% mineral reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.App..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman.
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Wellman Wellamid® XT1482-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Total PPH 12020 Polypropylene Homopolymer, Injection Molding Polypropylene PPH 12020 is a clarified high fluidity homopolymer with a melt flow index of 60 g/10 min.Polypropylene PPH 12020 has been designed with a very high stiffness and an outstanding transpa..
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman.
Flexural Modulus	1.80 GPa	261 ksi	2mm/min; ISO 178
Borealis Daplen™ EF261AI Polypropylene TPO Compound Daplen™ EF261AI is a 20 % mineral filled polypropylene compound intended for injection molding. This material has an excellent balance between impact strength and stiffness and is easy to process...
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Tipco Tipcolene® FX 995 - 10% Talc/Mineral Reinforced, Impact Modified Polypropylene Copolymer Compound with High Flow 10% Mineral Reinforced, High Flow, Impact Modified PP CopolymerApplications: Automotive Pillars & TrimsProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., ..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D 790
Cossa Polimeri ESTALUX 9206 Methyl Methacrylate Acrylonitrile Butadiene Styrene Plastic blend that combines impact properties of ABS with the excellent transparency of PMMABiomedical grade in line with US pharmacopeia class VI USP and European pharmacopeia cap. 3.2.2Information..
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Aclo Accutech Polypropylene Homopolymer HP0336T10L Talc Reinforced
Flexural Modulus	1.80 GPa	261 ksi	ASTM D790
Adell AD-10 Nylon 66, Ultra High Impact Data provided by Adell Plastics, Inc.
Flexural Modulus	1.80 GPa @Temperature 23.0 °C	261 ksi @Temperature 73.4 °F	ISO 178
Polykemi AB POLYfill PPH TS4020 Polypropylene Homopolymer, Mineral Reinforced Information provided by Polykemi AB
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman.
Flexural Modulus	1.80 GPa	261 ksi
Plastcom SLOVALEN PH 91 C 20 PP, 20% mineral filling FeaturesModified homopolymer and copolymer PP for injection moulding with the contenct of 20% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C..