- Honeywell ACLAR® Rx20E CTFE Homopolymer, Barrier Film
Honeywell ACLAR® Rx20E CTFE Homopolymer, Barrier Film
| Category | Polymer , Film , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Honeywell |
| Trade Name | ACLAR® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell ACLAR® Rx20E CTFE Homopolymer, Barrier Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: ACLAR® Rx20Eis a .8 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 g/cc | 2.11 g/cc | ASTM D1505 |
| Density | 2.10 g/cc | 0.0760 lb/in³ | Yield Density |
| Water Vapor Transmission | 0.0370 g/m²/day | 0.00238 g/100 in²/day | 77°F (25°C) / 60%RH; ASTM F1249 |
| 0.0620 g/m²/day | 0.00399 g/100 in²/day | 86°F (30°C) / 60%RH; ASTM F1249 | |
| 0.0690 g/m²/day | 0.00444 g/100 in²/day | 86°F (30°C) / 65% RH; ASTM F1249 | |
| 0.233 g/m²/day | 0.0150 g/100 in²/day | 104°F (40°C) / 75%RH; ASTM F1249 | |
| 0.295 g/m²/day | 0.0190 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 | |
| Thickness | 20.3 microns | 0.800 mil | |
| Surface Tension | >= 42 dynes/cm | >= 42 dynes/cm | treated side; ASTM F1249 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 90 - 150 % | 90 - 150 % | ASTM D882 |
| Film Elongation at Break, TD | 200 - 275 % | 200 - 275 % | ASTM D882 |
| Secant Modulus, MD | 1.131 - 1.551 GPa | 164.0 - 225.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.241 - 1.517 GPa | 180.0 - 220.0 ksi | ASTM D882 |
| Film Tensile Strength at Break, MD | 68.9 - 110 MPa | 10000 - 16000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 41.4 - 49.6 MPa | 6000 - 7200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 211 °C | 412 °F | crystalline melting point; ASTM D4591 |
| Shrinkage, MD | <= 12 % | <= 12 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= -12.0 % | <= -12.0 % | 300°F / 149°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 1.0 % | <= 1.0 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac® GT525 Acetal Homopolymer, 25% Glass Beads (discontinued **)
- Gouda Vuurvast AK 85 P1 Dense Refractory Brick
- Lanxess Pocan® BF 4130 XF 700051 PBT, 30% Glass Fiber
- Techmer ES HiFill® PA6/6 GF50 L UV 50% Glass Filled (Conditioned)
- Plenco 2369 Phenolic, Granular, Compression Molded
- Dow Corning HV 1650/50 SILICONE RUBBER
- Dow Corning SYL-OFF® 7016 CROSSLINKER
- ATI Allvac® Nickelvac® X- 751 UNS N07751 Nickel Superalloy
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/37%/280H5/AS4-3K
- Plaslok 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved