Lanxess Durethan® BM 240 H2.0 901510 Nylon 6, 40% Mineral
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BM 240 H2.0 901510 Nylon 6, 40% Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 40% mineral, isotopic properties, good heat-ageing resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 142 cm³/g | 142 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow | 23 g/10 min @Load 5.00 kg, Temperature 260 °C |
23 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Conditioned; ISO 527-1/-2 |
| 85.0 MPa | 12300 psi | ISO 527-1/-2 | |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-1/-2 |
| 40 % | 40 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | Conditioned; ISO 527-1/-2 |
| 6.00 GPa | 870 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 12.0 J/cm² @Temperature 23.0 °C |
57.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 3052 | 3052 | Puncture maximum force (N); ISO 6603-2 |
| 825 @Temperature -30.0 °C |
825 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 9.20 J | 6.79 ft-lb | ISO 6603-2 |
| 1.60 J @Temperature -30.0 °C |
1.18 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 1.60 J @Temperature -30.0 °C |
1.18 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 200 °C | 392 °F | 50°C/h 50N; ISO 306 |
| Oxygen Index | 26 % | 26 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.4 @Frequency 100 Hz |
4.4 @Frequency 100 Hz |
IEC 60250 | |
| 4.7 @Frequency 1.00e+6 Hz |
4.7 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 15 @Frequency 100 Hz |
15 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| 38.0 kV/mm | 965 kV/in | Conditioned; IEC 60243-1 | |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.10 @Frequency 1.00e+6 Hz |
0.10 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.25 @Frequency 100 Hz |
0.25 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 525 V | 525 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6,MHR,14-060,MD40 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Nye Lubricants 855B (FG) Synthetic Oil
- Chi Mei Wonderloy® PC-175D PC/ABS Alloy (discontinued **)
- Karina E 70/222-D-IS-SD Clear PVC Compound
- SABIC Innovative Plastics NORYL SA9000 PPE (Asia Pacific)
- Techmer ES Electrablend® PEI 04008 MB
- Solvay Specialty Polymers Tecnoflon® FOR TF Fluoroelastomer
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Sulfur
- ExxonMobil Santoprene® 151-70W256 Thermoplastic Vulcanizate - Flame Retardant
- Asahi Kasei Tenac®-C 4513 Copolymer Acetal Resin
- 3M Novec™ 72FL Engineered Fluid
Copyright © lookpolymers.com All Rights Reserved