- Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade
Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade
| Category | Polymer , Thermoplastic , Acrylic (PMMA) |
| Manufacturer | Sumitomo Chemical |
| Trade Name | Sumipex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Chemical Sumipex® BF3 Acrylic Resin, GP Blow Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product CharacteristicsExcellent WeatherabilityHigh TransparencyGood Heat ResistanceInformation provided by Calsak Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa @Thickness 3.17 mm |
10000 psi @Thickness 0.125 in |
Type I; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa @Thickness 3.17 mm |
16000 psi @Thickness 0.125 in |
Type I; ASTM D790 |
| Flexural Modulus | 3.10 GPa @Thickness 3.17 mm |
450 ksi @Thickness 0.125 in |
Type I; ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
0.790 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C @Thickness 3.17 mm |
201 °F @Thickness 0.125 in |
annealed; ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 0.50 % | <= 0.50 % | ASTM D1003 |
| Transmission, Visible | 93 % | 93 % | Total light Transmission; ASTM D1003 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1494T PC Copolymer
- Lehmann & Voss LUVOCOM® 20-0791 Polyphthalamide, with glass fiber and PTFE
- Lord Adhesives Metech 3503 Palladium Silver Conductor Composition
- Momentive Performance Materials TSE326 Red Adhesive Sealant, Non-Corrosive Flowable High Temperature
- Dow BETAFOAM™ 87100/87120
- Fainplast Compounds HAX HF 3622 Halogen Free PVC
- ConocoPhillips Synterra™ 3 Hydraulic Oil, AGMA No.3
- Multibase Multi-Flam™ 0102 Natural PP Polypropylene
Copyright © lookpolymers.com All Rights Reserved