Kolon SPESIN® KP212G30VO G/F Reinforced & Retardant PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Kolon |
| Trade Name | SPESIN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon SPESIN® KP212G30VO G/F Reinforced & Retardant PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High heat stability, outstanding abrasion resistance, excellent electrical properties, good surface gloss, low water absorption, excellent chemical resistance, good processabilityInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 132 MPa | 19200 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 206 MPa | 29900 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm | 1.47 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 224 °C | 435 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Raschig Group 2568 AMC
- SABIC Innovative Plastics Lexan® VR2820 PC (Europe-Africa-Middle East)
- Total Finathene® LL 4010 FH 18 LLDPE film (discontinued **)
- Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Dry)
- Sharadaa Ceramics REFCAST ULCC90 Low Cement Castables
- SABIC Innovative Plastics LNP LUBRILOY ZX06315 PPE+SEBS+Polyolefin (Asia Pacific)
- Teknor Apex Sinvicomp SFC 7500 Polyvinyl Chloride, Flexible
- Ashley Polymers Ashlene® P260WO PPO
- PlastiComp Complet® LCF50 - PA66 MT Nylon 66, 50% Long Carbon Fiber Reinforced, Impact Modified
Copyright © lookpolymers.com All Rights Reserved