LG Chemical LUMID LW4203A(W) PA6+GF/MF20%, Low Warpage
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID LW4203A(W) PA6+GF/MF20%, Low Warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA6+GF/MF20%, Low WarpageApplication: Automotive Parts (Engine Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.012 cm/cm @Thickness 3.20 mm |
0.0070 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 103 MPa @Thickness 3.20 mm |
14900 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Elongation at Break | 9.0 % @Thickness 3.20 mm |
9.0 % @Thickness 0.126 in |
5mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 3.92 GPa @Thickness 3.20 mm |
569 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.918 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C @Thickness 6.40 mm |
356 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 1.00 mm |
533 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 265 °C | 464 - 509 °F | Injection Molding |
| Front Barrel Temperature | 240 - 265 °C | 464 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 275 °C | 482 - 527 °F | Injection Molding |
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® Verdi VR A3000 AE Expandable Polystyrene - Flame Retardant
- SABIC Innovative Plastics Cycolac® INP563 ABS+SAN
- Palm Labs Adhesives TURBO FUSE SERIES 190 CLEAR FLEXIBLE (4000 Viscosity) Rapid Bonding Adhesive
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature
- Kazanorgsintez Cosintol 242
- Sylvin Technologies 8600-85 Clear PVC Extrusion Compound
- SABIC Innovative Plastics LNP STAT-KON Noryl_NC2525 PPE+HIPS (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA (Asia Pacific)
- Asahi Glass Fluon® XAD911 PTFE Aqueous Dispersion
- Ashley Polymers Ashlene® 528L2 Nylon 66
Copyright © lookpolymers.com All Rights Reserved