Techmer ES Plastiblend® ABS/PA 1700 B2
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Techmer ES Plastiblend® ABS/PA 1700 B2.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAppearance: Natural ColorProcessing Method: ExtrusionInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm <br>@Thickness 3.17 mm |
0.0060 in/in <br>@Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 1.0 g/10 min <br>@Load 3.80 kg,<br> Temperature 230 °C |
1.0 g/10 min <br>@Load 8.38 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Break | 55 % | 55 % | ASTM D638 |
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm <br>@Thickness 3.17 mm |
12.0 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.6 °C | 168 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB <br>@Thickness 1.50 mm |
HB <br>@Thickness 0.0591 in |
Users viewing this material also viewed the following:
- RheTech Products P250-00UV Polypropylene Copolymer, UV Stabilized, Natural
- Ovation Polymers UTTAP QU BM513 GF BM Nylon, 13% Glass Reinforced
- Polymax® Maxelast® F7880 TPE, Fire Retardant
- Hong Kun Group UV 944 UV Absorber
- Universal Wire Works 182 Nickel Alloy Welding Wire
- ThyssenKrupp 12Ni5 Structural Steel
- Hexcel® Redux® 319 High Performance Modified Epoxy Film Adhesive (0.07 psf)
- Goodfellow Polyvinyl Fluoride (PVF) Film
- Addcomp ADD-VANCE® FR 243 Halogen-free flame retardant masterbatch, PP based
Copyright © lookpolymers.com All Rights Reserved