Lanxess Durethan® BM 240 000000 Nylon 6, Mineral Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BM 240 000000 Nylon 6, Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, injection molding, 40% mineral, isotopic properties, low warpageInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Moisture Absorption at Equilibrium 1.9 %
1.9 %
50% RH; ISO 62
Water Absorption at Saturation 6.0 %
6.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.0017 cm/cm
0.0017 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 294-4
0.0125 cm/cm
0.0125 in/in
150x105x3; 280°C / MT 80°C; 500 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 294-4
0.0122 cm/cm
0.0122 in/in
150x105x3; 280°C / MT 80°C; 500 bar; ISO 294-4
Mechanical Properties Metric English Comments
Ball Indentation Hardness 85.0 MPa
12300 psi
ISO 2039-1
205 MPa
29700 psi
ISO 2039-1
Tensile Strength at Break 55.0 MPa
7980 psi
cond.; ISO 527-1, -2; 5 mm/min
85.0 MPa
12300 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 10 %
10 %
ISO 527-1, -2; 5 mm/min
40 %
40 %
ISO 527-1, -2; 5 mm/min
Tensile Modulus 2.20 GPa
319 ksi
cond.; ISO 527-1, -2; 1 mm/min
5.80 GPa
841 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 65.0 MPa

@Strain 8.00 %
 9430 psi

@Strain 8.00 %
 cond., 2 mm/min; ISO 178-A
150 MPa

@Strain 5.00 %
 21800 psi

@Strain 5.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 60.0 MPa

@Strain 3.50 %
 8700 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
145 MPa

@Strain 3.50 %
 21000 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 2.00 GPa
290 ksi
cond., 2 mm/min; ISO 178-A
5.50 GPa
798 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) 75.0 kJ/m²

@Temperature -30.0 °C
 35.7 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
85.0 kJ/m²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
100 kJ/m²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
8.00 J/cm²

@Temperature -30.0 °C
 38.1 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
14.0 J/cm²

@Temperature 23.0 °C
 66.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
1.20 J/cm²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Puncture Energy 65.0 J

@Temperature 23.0 °C
 47.9 ft-lb

@Temperature 73.4 °F
 cond.; ISO 6603-2
3.00 J

@Load <=74.2 kg,
Temperature -30.0 °C
 2.21 ft-lb

@Load <=164 lb,
Temperature -22.0 °F
 d.a.m.; ISO 6603-2
20.0 J

@Load <=309.1 kg,
Temperature 23.0 °C
 14.8 ft-lb

@Load <=681.4 lb,
Temperature 73.4 °F
 d.a.m.; ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 33.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 38.9 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
ISO 75-1, -2
Vicat Softening Point >= 200 °C

@Load 5.10 kg
 >= 392 °F

@Load 11.2 lb
 120°C/hour; ISO 306
>= 200 °C

@Load 5.10 kg
 >= 392 °F

@Load 11.2 lb
 50°C/hour; ISO 306
Glow Wire Test 650 °C

@Diameter 2.00 mm
 1200 °F

@Diameter 0.0787 in
 GWFI; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
290 °C
554 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, MHR, 14-060, MD40