Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 35 H3.0 000000 Nylon 6, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 35% glass fibers, injection molding, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 6.5 % | 6.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00030 cm/cm | 0.00030 in/in | Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577 |
| 0.00050 cm/cm | 0.00050 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 | |
| 0.0016 cm/cm | 0.0016 in/in | 150x105x3; 280°C / MT 80°C; 500 bar; ISO 2577 | |
| 0.0023 cm/cm | 0.0023 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.00070 cm/cm | 0.00070 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0010 cm/cm | 0.0010 in/in | Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577 | |
| 0.0068 cm/cm | 0.0068 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| 0.0081 cm/cm | 0.0081 in/in | 150x105x3; 280°C / MT 80°C; 500 bar; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 190 MPa | 27600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 3.0 % | 3.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 5.0 % | 5.0 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 6.80 GPa | 986 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 11.0 GPa | 1600 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 180 MPa @Strain 5.00 % |
26100 psi @Strain 5.00 % |
cond., 2 mm/min; ISO 178-A |
| 290 MPa @Strain 4.00 % |
42100 psi @Strain 4.00 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 160 MPa @Strain 3.50 % |
23200 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| Flexural Modulus | 5.90 GPa | 856 ksi | cond., 2 mm/min; ISO 178-A |
| 10.7 GPa | 1550 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 22.0 kJ/m² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | d.a.m.; ISO 180-1U |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 7.50 J/cm² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA | |
| Tensile Creep Modulus, 1 hour | 6000 MPa | 870000 psi | cond.; ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 4900 MPa | 711000 psi | cond.; ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1, -2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Vicat Softening Point | >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | cond.; IEC 60093 |
| 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | d.a.m.; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | cond.; IEC 60093 |
| 1.00e+14 ohm | 1.00e+14 ohm | d.a.m.; IEC 60093 | |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 5.0 @Frequency 1.00e+6 Hz |
5.0 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 15 @Frequency 100 Hz |
15 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
cond.; IEC 60243-1 |
| 40.0 kV/mm @Thickness 1.00 mm |
1020 kV/in @Thickness 0.0394 in |
d.a.m.; IEC 60243-1 | |
| Dissipation Factor | 0.0070 @Frequency 100 Hz |
0.0070 @Frequency 100 Hz |
d.a.m.; IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
d.a.m.; IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
cond.; IEC 60250 | |
| 0.20 @Frequency 100 Hz |
0.20 @Frequency 100 Hz |
cond.; IEC 60250 | |
| Comparative Tracking Index | 525 V | 525 V | d.a.m.; Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability Test | passed | ISO 3795; US-FMVSS302 |
| ISO Shortname | ISO 1874-PA 6, GHR, 14-110, GF35 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRC 2 LI PA6, flame retardant
- Total Lacqtene® 2004 TN 52 HDPE pipe (discontinued **)
- Permabond HH040 Pure NSF 61 Approved Anaerobic Retainer
- Trelleborg Sealing Solutions HiMod® 924 Thermoplastic Bearing
- Dow Nordel® IP 4770R General Purpose Compound
- Azoty Tarnow™ Tarnamid® T-27 CF10 Polyamide 6 10% Carbon Fiber - Antistatic and Electroconductive
- 3M GM613 Ultra Soft Gripping Material
Copyright © lookpolymers.com All Rights Reserved