- Menzolit Menzolit® BMC 1100 Unsaturated Polyester UP
Menzolit Menzolit® BMC 1100 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 1100 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 1100 is a special BMC for high strength application. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. The selection of the resin and glass fibres provide good properties at high mechanical loads even if they are cyclic or impact like. The fire retardancy level HB according to the UL 94 is achieved. Typical applications are functional components for the automotive industry and chemical engineering. The material is especially suited for highly loaded or fast moving components.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.00030 cm/cm | 0.00030 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 40.0 MPa @Temperature 22.0 °C |
5800 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 40.0 MPa @Temperature 22.0 °C |
5800 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 130 MPa @Temperature 22.0 °C |
18900 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 9.00 GPa @Temperature 22.0 °C |
1310 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.00 GPa | 725 ksi | in plane |
| Charpy Impact, Notched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 150 °C | >= 302 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 162 °C | 324 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 160 °C | 275 - 320 °F | Injection moulding, matched metal die |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FG 306 Hexene Copolymer Linear Low Density Polyethylene
- Polimeri Europa Europrene Latice® 5570 Styrene - Butadiene Copolymer
- PolyOne Maxxam™ FR PE 152 Polyethylene, Unspecified (PE, Unspecified)
- Omni Plastics OmniLon™ 6 PA6 WF10 Mineral Filled Nylon
- Lucas-Milhaupt Silvally® 45 Flux Coated Rod Brazing Alloy
- H.C. Starck Amperit® 720.054 Blended Chromium Oxide-Aluminum Oxide-Titanium Oxide 80-17-3 (Cr2O3-Al2O3-TiO2)
- Zircar Ceramics SALI-2 Alumina Insulation
- Trelleborg R490 Commercial Natural Rubber Polyisoprene
- Dow Latex XZ 92219.00 Experimental Latex
- DuPont Performance Polymers Hytrel® RS R4275 BK316 Polyester Elastomer TPC-ET
Copyright © lookpolymers.com All Rights Reserved