Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® PP4410 PP, Fire Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 29.4 MPa | 4270 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Flexural Yield Strength | 34.3 MPa | 4980 psi | ASTM D790 |
| Flexural Modulus | 1.08 GPa | 156 ksi | ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**)
- Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA) (Unverified Data**)
- Henkel Hysol EA 9681 Film Adhesive
- GEHR Plastics PA 6.6 Nylon 6.6, Dry
- Taiwan PU Corporation TPUI-L90 Low Temperature Resistance, Injection Molding Polyester Base TPU
- Star Plastics PC20NBR Molding Grade PC with Release
- Asahi Kasei Thermylene® P-40TC-8100 Chemically Coupled Polypropylene Compound, 40% Talc Filled
- Quantum Composites QC-8770 63% Glass Fiber Hybrid Vinyl Ester SMC (discontinued **)
- Formosa Plastics Formolene® 4142N Injection Molding Polypropylene
Copyright © lookpolymers.com All Rights Reserved