- Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified
Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.169 g/cc | 1.169 g/cc | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00090 cm/cm | 0.00090 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0071 cm/cm | 0.0071 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0015 cm/cm | 0.0015 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0075 cm/cm | 0.0075 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | cond.; ISO 527-1, -2; 5 mm/min |
| 80.0 MPa | 11600 psi | d.a.m.; ISO 527-1, -2; 5 mm/min | |
| Elongation at Break | 5.0 % | 5.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| 15 % | 15 % | cond.; ISO 527-1, -2; 5 mm/min | |
| Tensile Modulus | 2.00 GPa | 290 ksi | cond.; ISO 527-1, -2; 1 mm/min |
| 4.50 GPa | 653 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min | |
| Flexural Strength | 75.0 MPa @Strain 8.00 % |
10900 psi @Strain 8.00 % |
cond., 2 mm/min; ISO 178-A |
| 135 MPa @Strain 5.50 % |
19600 psi @Strain 5.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Yield Strength | 55.0 MPa @Strain 3.50 % |
7980 psi @Strain 3.50 % |
cond., 2 mm/min; ISO 178-A |
| 120 MPa @Strain 3.50 % |
17400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A | |
| Flexural Modulus | 2.10 GPa | 305 ksi | cond., 2 mm/min; ISO 178-A |
| 4.10 GPa | 595 ksi | d.a.m., 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A |
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1A | |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A | |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 180-1U | |
| 65.0 kJ/m² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U | |
| 90.0 kJ/m² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 180-1U | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU | |
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eU | |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
cond.; ISO 179-1eA | |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA | |
| 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
cond.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 219 °C | 426 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6-HI, GHR, 14-040, GF15 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 950A PC (Europe-Africa-Middle East)
- Overview of materials for Polycarbonate/Thermoplastic Polyurethane Blend
- SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific)
- Solvay TECHNYL® A 20 V25 PA66, 25% glass fiber, Conditioned
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- Chesterton 218 HDP Liquid alkaline degreaser
- ConocoPhillips Hydroclear Diamond Class® 32 AW Turbine Oil
- 3M Scotchcal™ ElectroCut™ 413 Graphic Film
- BCC Products BC 8990 Polyurethane Elastomer
- A. Schulman POLYFORT™ PP 1329 UV Stabilized, Medium Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved