SABIC Innovative Plastics LNP LUBRICOMP KA000M POM (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KA000M POM (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* KA000M is a compound based on Acetal Copolymer resin containg Aramide and Proprietary Lubricant. Added features include Internally Lubricated.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.025 cm/cm
0.025 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 41.0 MPa
5950 psi
5 mm/min; ISO 527
Elongation at Yield 7.4 %
7.4 %
5 mm/min; ISO 527
Tensile Modulus 2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 68.0 MPa
9860 psi
2 mm/min; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Coefficient of Friction, Dynamic 0.21
0.21
ASTM D3702 Modified
Coefficient of Friction, Static 0.21
0.21
ASTM D3702 Modified
K (wear) Factor 18.1 x 10-8 mm³/N-M
9.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 114 µm/m-°C

@Temperature 23.0 - 60.0 °C
 63.3 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 116 µm/m-°C

@Temperature 23.0 - 60.0 °C
 64.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af