Lanxess Durethan® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AM 40 X H2.0 901510 Nylon 66, Glass Fiber/Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 40% glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warpInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.00050 cm/cm
0.00050 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0040 cm/cm
0.0040 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0010 cm/cm
0.0010 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0097 cm/cm
0.0097 in/in
60x60x2; 290°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
cond.; ISO 527-1, -2; 5 mm/min
170 MPa
24700 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 2.5 %
2.5 %
d.a.m.; ISO 527-1, -2; 5 mm/min
6.5 %
6.5 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 6.50 GPa
943 ksi
cond.; ISO 527-1, -2; 1 mm/min
12.2 GPa
1770 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 140 MPa

@Strain 6.00 %
 20300 psi

@Strain 6.00 %
 cond., 2 mm/min; ISO 178-A
250 MPa

@Strain 3.00 %
 36300 psi

@Strain 3.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 125 MPa

@Strain 3.50 %
 18100 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 6.10 GPa
885 ksi
cond., 2 mm/min; ISO 178-A
11.0 GPa
1600 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
13.0 kJ/m²

@Temperature 23.0 °C
 6.19 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Izod Impact, Unnotched (ISO) 50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1U
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
55.0 kJ/m²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1U
Charpy Impact Unnotched 5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched <= 1.00 J/cm²

@Temperature 23.0 °C
 <= 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
<= 1.00 J/cm²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
Thermal Properties Metric English Comments
Melting Point 263 °C
505 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) >= 250 °C
>= 482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
290 °C
554 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 66, GHR, 14-120, (GF+MD)40