LG Chemical LUPOY RF3208F PC, Halogen Free Flame Retardance
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY RF3208F PC, Halogen Free Flame Retardance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardance, Light Reflectance, White Color OnlyApplication: LCD Back Light Unit partsCAS: 103598-77-2 and 13463-67-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.9 MPa @Thickness 3.20 mm |
7820 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 70 % @Thickness 3.20 mm |
70 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 93.2 MPa @Thickness 3.20 mm |
13500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa @Thickness 3.20 mm |
370 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 3.43 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 6.43 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 230 °C @Thickness 6.40 mm |
>= 446 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C @Thickness 1.60 - 1.70 mm |
176 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 1.60 - 1.70 mm |
176 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical without Impact | 80.0 °C @Thickness 1.60 - 1.70 mm |
176 °F @Thickness 0.0630 - 0.0669 in |
|
| Flammability, UL94 | V-0 @Thickness 1.60 - 1.70 mm |
V-0 @Thickness 0.0630 - 0.0669 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Middle Barrel Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Front Barrel Temperature | 260 - 290 °C | 500 - 554 °F | Injection Molding |
| Nozzle Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | Injection Molding |
| Mold Temperature | 45.0 - 80.0 °C | 113 - 176 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 5.00 - 7.00 hour | 5.00 - 7.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Park Electrochemical Nelco® NH9450 PTFE Laminate, Woven-Glass and Ceramic Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP BX03658N SAN
- Idemitsu Kosan Xarec® WA 550 SPS, 30% Glass Filled
- Grupo Repol Dinalon® B1S25 G30PV0 30% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 6
- Multibase Multibatch® MP 52711 BOPP White Pearlised Film
- SABIC Innovative Plastics ULTEM 2212R PEI (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- EMS-Grivory Grivory® TSG-35/4 H black 9836 PA666-GF35
- EMS-Grivory Grivory® XE 4128 black 9221 PA610
Copyright © lookpolymers.com All Rights Reserved