Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D 1238 |
SABIC Innovative Plastics Geloy XTWE480 ASA (Asia Pacific) Anti-scratch Geloy grade with excellent weatherability, high flow, and good surface quality. XTWE480 is available in various colours.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
PolyMirae Moplen HP563S Fiber (Spunbond) Grade Polypropylene Moplen HP563S is the controlled rheology polypropylene homopolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen HP563S is a homopolymer typically used in spunb.. |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 260 °C |
38 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
Lanxess Pocan® T 7331 POS151 000000 PBT + PET, 30% Glass Fiber
(discontinued **) PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized |
|||
Melt Flow | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
|
PTS Tristar® PC-10R-CL02(V38) 38 MFI Polycarbonate with Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H38G-01 Polypropylene Homopolymer, Fiber Grade
(discontinued **) Suggested fabrication methods: Fiber spinningFeatures: Very high speed spinning, Low gas fadeTypical applications: Spunbound fabricsComplies with FDA specification, Title 21, CFR 177.1520.Typical pr.. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
M. Holland Company PP720 Polypropylene Homopolymer Gas-fading resistantHomopolymerGood processabilityGood UV resistanceApplications: FabricsSpunbond non-wovensYarn |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
Ineos ABS Lustran® ABS 250 Injection Molding Grade Lustran® ABS 250 has standard impact strength, high flow, and is injection molding grade. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H38G-02 Polypropylene Homopolymer This is a polypropylene homopolymer for general purpose injection molding and high speed spinning applications. It is useful for spun bonded nonwovens and partially oriented yarn (POY). This mater.. |
|||
Melt Flow | 38 - 50 g/10 min @Load 2.16 kg, Temperature 190 °C |
38 - 50 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238-00 |
Ipiranga Petrochem PCC 4414 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 260 °C |
38 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® DP 1801/30 H3.0 000000 Nylon 6, 30% Milled Glass Fiber PA 6, injection molding grade, 30% milled fibers, UL 94V-2 at 0.8 mm, max. temperature in glow wire test: 960 °C at 0,75 mm, "halogen-free", good heat-ageing resistanceApplication Examples: Medic.. |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 260 °C |
38 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
Lanxess Pocan® T 7331 000000 PBT + PET, 30% Glass Fiber PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
LG Chemical LUPOL HF5157 PP+Rubber+MF, High Flow and Stiffness, High Impact Description: Injection Molding, PP+Rubber+MF, High Flow and Stiffness, High Impact, Good Weatherability, Scratch ResistanceApplication: Automotive Exterior (Slim wall Bumper Fascia)Information provi.. |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
Styrolution Novodur® 250 ABS Novodur 250 is an injection molding grade of ABS with standard impact strength, high flow and high gloss.Information provided by Styrolution |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 250 °C |
38 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® HN-1064 PC, Unreinforced FR PC material that is applied to other resin for mobile phone chargersInformation provided by Samsung Cheil Industries. |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
Samsung Cheil Industries Infino® NE-1050 PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 250 °C |
38 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
Samyang Tribit® 1500G30K PBT, Reinforced Impact Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1500G30K is a reinforced, impact grade.Appl.. |
|||
Melt Flow | 38 g/10 min | 38 g/10 min | ASTM D1238 |
ExxonMobil Escor™ 5200 Ethylene Acrylic Acid Copolymer Resin Product Description: Escor 5200 is an ethylene acrylic acid copolymer with a high comonomer content. Escore 5200 can be used pure or as a component in blend formulations for bonding applications whe.. |
|||
Melt Flow | 38 g/10 min @Temperature 230 °C |
38 g/10 min @Temperature 446 °F |
ASTM D1238 |
Dow 5D49 Polypropylene Resin DOW 5D49 is intended for use fiber spinning processes. It is well suited for spunbond non-woven applications.Information provided by DowDow Announced Sale of Global Polypropylene Business to Braske.. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg |
38 g/10 min @Load 4.76 lb |
Melt flow ratio I10/I2 is 8.5. |
Dow HDPE 38152M High Density Polyethylene DOW HDPE 38152M resin is a medium molecular weight distribution copolymer designed to offer good impact strength and stress crack resistance with excellent toughness. This resin has excellent proces.. |
|||
Melt Flow | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
E-Polymers TEKANATE® G7038 High Easy Molding Polycarbonate Modified Poly Carbonate: TEKANATE is a modified PC by improving polycarbonate resins with features of halogen-free flammability, transparency, impact resistance and reinforced fiberglass. It shows .. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM-D1238 |
Braskem H 125 HOMO Polypropylene Homopolymer H 125 is a high melt flow rate homopolymer designed for nonwoven by spunbonded processing. It is used in fiber extrusion processing. This resin features excellent processing, allowing increased line.. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Braskem MV-501 Impact Copolymer Polypropylene Description: Long term heat stability, nucleated, excellent processability.Applications: Suggested uses include compounding, thin-walled injection molding.Process: Injection Molding.This resin meets.. |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
Bhansali Engineering Abstron MIF-35 ABS Injection Molding Grade High Impact, Medium, High Flow, General PurposeInformation provided by Bhansali |
|||
Melt Flow | 38 g/10 min @Load 10.0 kg, Temperature 220 °C |
38 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
Bhansali Engineering Abstron AN480V2 Flame Retardant ABS Grade Information provided by Bhansali |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
ExxonMobil Exxtral™ CNW 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for injection molded automotive interior trim applications requiring low warpage.Availability: Africa & Middle East, Asia Pac.. |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 265 °C |
38 g/10 min @Load 11.0 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
SABIC Innovative Plastics Valox® V9235 PET (Europe-Africa-Middle East) Valox heat stabilized, 15% Glass filled grade with mold release based on recycle PET. This grade is typically applied for business Machines applicationsThis data was supplied by SABIC-IP for the Eu.. |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 260 °C |
38 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
Lanxess Durethan® BM 25 FN20 DUS013 000000 Nylon 6, 25% Mineral PA 6, injection molding grade, 25% mineral, UL94V-2 off 0.75 mm, max. temp. glow wire test:960°C off 0.8 mm, free from halogen, optimized for laser marking at 1064 nm, |
|||
Melt Flow | 38 g/10 min @Load 5.00 kg, Temperature 190 °C |
38 g/10 min @Load 11.0 lb, Temperature 374 °F |
|
Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 62 Shore A
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® 602 is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its broad molecular weight distribution, Finaprene® 60.. |
|||
Melt Flow | 38 g/10 min @Load 2.16 kg, Temperature 230 °C |
38 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Ineos H38K-00 Polypropylene Homopolymer, Fiber Grade
(discontinued **) Suggested fabrication methods: Fiber spinningFeatures: Very high speed spinning, Low gas fade, Low smokeTypical applications: Spunbound fabricsComplies with FDA specification, Title 21, CFR 177.1520.. |