SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LC008E PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LC008E is a compound based on Polyetheretherketone resin containing 40% Carbon Fiber. Added features of this material include: Easy Molding, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ASTM D792 |
| 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.00050 cm/cm @Time 86400 sec |
0.00050 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec |
0.0073 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 240 MPa | 34800 psi | ASTM D638 |
| 242 MPa | 35100 psi | ISO 527 | |
| Tensile Strength, Yield | 240 MPa | 34800 psi | ASTM D638 |
| 242 MPa | 35100 psi | ISO 527 | |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Elongation at Yield | 1.3 % | 1.3 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 30.52 GPa | 4427 ksi | 1 mm/min; ISO 527 |
| 33.09 GPa | 4799 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 352 MPa | 51100 psi | ISO 178 |
| 365 MPa | 52900 psi | ASTM D790 | |
| Flexural Modulus | 26.88 GPa | 3899 ksi | ASTM D790 |
| 27.5 GPa | 3990 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.04 J/cm | 13.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 7.00 µm/m-°C @Temperature -40.0 - 40.0 °C |
3.89 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 7.20 µm/m-°C @Temperature -40.0 - 40.0 °C |
4.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 338 °C | 640 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 338 °C @Thickness 3.20 mm |
640 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 326 °C | 619 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 322 °C @Thickness 3.20 mm |
612 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Dry
- Metabolix Mirelâ„¢ I6001 Biobased Polymeric Modifier
- Mitsui UNISTOLEâ„¢ R-120K Polyolefinic Primer/ Adhesive
- Universal Wire Works Haynes 25 (L-605) (AMS 5796) Filler Metal
- Goodfellow T1-Thermocouple Alloy
- ExxonMobil SAE 40 Mobilgard M50
- Fainplast Compounds GSK 78 Flexible PVC, Injection Molding, Lead Free
- Arlon R3758R0055 0.065" Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved