LG Chemical LUPOY GP5006AF PC/ABS, Flame Retardant

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical LUPOY GP5006AF PC/ABS, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description: Injection Molding, PC/ABS, Flame RetardantApplication: Electric and Electronic Housing and ComponentsCAS: 103598-77-2, 9003-56-9, 68928-70-1 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0080 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 6.0 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 51.0 MPa
<br>@Thickness 3.20 mm
 7400 psi
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 60 %
<br>@Thickness 3.20 mm
 60 %
<br>@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 78.5 MPa
<br>@Thickness 3.20 mm
 11400 psi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.16 GPa
<br>@Thickness 3.20 mm
 313 ksi
<br>@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched 4.41 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 8.27 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 104 °C
<br>@Thickness 6.40 mm
 219 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 85.0 °C
<br>@Thickness >=0.750 mm
 185 °F
<br>@Thickness >=0.0295 in
85.0 °C
<br>@Thickness >=1.70 mm
 185 °F
<br>@Thickness >=0.0669 in
85.0 °C
<br>@Thickness >=3.00 mm
 185 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 75.0 °C
<br>@Thickness >=0.750 mm
 167 °F
<br>@Thickness >=0.0295 in
75.0 °C
<br>@Thickness >=1.70 mm
 167 °F
<br>@Thickness >=0.0669 in
75.0 °C
<br>@Thickness >=3.00 mm
 167 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 75.0 °C
<br>@Thickness >=0.750 mm
 167 °F
<br>@Thickness >=0.0295 in
75.0 °C
<br>@Thickness >=1.70 mm
 167 °F
<br>@Thickness >=0.0669 in
75.0 °C
<br>@Thickness >=3.00 mm
 167 °F
<br>@Thickness >=0.118 in
Flammability, UL94 V-0
<br>@Thickness >=0.750 mm
 V-0
<br>@Thickness >=0.0295 in
V-0
<br>@Thickness >=1.70 mm
 V-0
<br>@Thickness >=0.0669 in
5VB
<br>@Thickness >=3.00 mm
 5VB
<br>@Thickness >=0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Middle Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Front Barrel Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Nozzle Temperature 245 - 275 °C
473 - 527 °F
Injection Molding
Melt Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding