Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® TH-1100 PC, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 17 g/10 min

@Load 10.0 kg,
Temperature 250 °C
 17 g/10 min

@Load 22.0 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 63.7 MPa
9250 psi
5 mm/min; ASTM D638
Flexural Strength 94.1 MPa
13600 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.16 GPa
313 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched >= 0.490 J/cm

@Thickness 3.17 mm
 >= 0.918 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 6.40 mm
 266 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 144 °C
291 °F
B/50; ISO R306
Flammability, UL94 V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 3.20 mm
 2.0 %

@Thickness 0.126 in
 ASTM D1003
Transmission, Visible 86 %

@Thickness 3.20 mm
 86 %

@Thickness 0.126 in
 ASTM D1003