LG Chemical LUPOY GN1000F PC, Halogen Free, Flame Retardant, Transparency

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN1000F PC, Halogen Free, Flame Retardant, Transparency.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 181028-79-5Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 72.6 MPa

@Thickness 3.20 mm
 10500 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 50 %

@Thickness 3.20 mm
 >= 50 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 118 MPa

@Thickness 3.20 mm
 17100 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.65 GPa

@Thickness 3.20 mm
 384 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 0.343 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 0.643 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 6.40 mm
 203 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=2.50 mm
 176 °F

@Thickness >=0.0984 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=2.50 mm
 176 °F

@Thickness >=0.0984 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=2.50 mm
 176 °F

@Thickness >=0.0984 in
80.0 °C

@Thickness >=3.00 mm
 176 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=2.50 mm
 V-0

@Thickness >=0.0984 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Optical Properties Metric English Comments
Transmission, Visible 89 %
89 %
ASTM D1003
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 255 °C
455 - 491 °F
Injection Molding
Middle Barrel Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Front Barrel Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Nozzle Temperature 250 - 265 °C
482 - 509 °F
Injection Molding
Melt Temperature 230 - 265 °C
446 - 509 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding