Ineos N05U-00 Polypropylene Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Ineos Olefins & Polymers USA
Trade Name
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Ineos N05U-00 Polypropylene Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

This is an extrusion-grade nucleated impact copolymer polypropylene resin designed for fiber optic buffer tube applications in the protection of glass fibers. It also has an excellent impact/stiffness property balance and provides the high compression strength required to meet the Bellcore GR-20-CORE standard (Generic Requirements for Optical Fiber and Fiber Optic Cable).ApplicationsBuffer tubesFiller rodsCore jacketsBenefitsOxidative stabilityUV stabilizedESCRGood balance of stiffness and impact strengthInformation provided by Ineos Olefins & Polymers USA

Physical Properties	Metric	English	Comments
Melt Flow	5.0 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 Â°C	5.0 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	81	81	ASTM D785
Tensile Strength, Yield	27.6 MPa <br>@Temperature 23.0 Â°C	4000 psi <br>@Temperature 73.4 Â°F	ASTM D638
Elongation at Break	>= 500 %	>= 500 %	ASTM D638
Flexural Modulus	1.31 GPa <br>@Temperature 23.0 Â°C	190 ksi <br>@Temperature 73.4 Â°F	D790B
Izod Impact, Notched	0.534 J/cm <br>@Temperature -20.0 Â°C	1.00 ft-lb/in <br>@Temperature -4.00 Â°F	1/8'' notched bar; ASTM D256
	NB <br>@Temperature 23.0 Â°C	NB <br>@Temperature 73.4 Â°F	1/8'' notched bar; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	113 Â°C	235 Â°F	ASTM D648

Descriptive Properties	Value	Comments
Process	Extrusion