DuPont Performance Polymers Zytel® 70G25HSLR BK099 Nylon 66 (Unverified Data**)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer	DuPont Performance Polymers
Trade Name	Zytel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Zytel® 70G25HSLR BK099 Nylon 66 (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

25% Glass Reinforced Heat Stabilized Hydrolysis Resistant Polyamide 66 Zytel 70G25HSLR BK099 is a 25% glass fiber reinforced heat stabilized hydrolysis resistant polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in³	DAM; ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	120 MPa	17400 psi	50%RH; ISO 527-1/-2
	180 MPa	26100 psi	DAM; ISO 527-1/-2
Elongation at Break	3.0 %	3.0 %	DAM; ISO 527-1/-2
	6.0 %	6.0 %	50%RH; ISO 527-1/-2
Tensile Modulus	6.10 GPa	885 ksi	50%RH; ISO 527-1/-2
	8.40 GPa	1220 ksi	DAM; ISO 527-1/-2
Charpy Impact Unnotched	6.00 J/cm²	28.6 ft-lb/in²	DAM; ISO 179/1eU
	8.00 J/cm²	38.1 ft-lb/in²	50%RH; ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	DAM; ISO 179/1eA
	1.10 J/cm²	5.23 ft-lb/in²	50%RH; ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	262 °C	504 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	252 °C @Thickness 1.50 mm	486 °F @Thickness 0.0591 in	DAM; ISO 75-1/-2
Flame Spread	27 mm/min @Thickness 1.00 mm	1.1 in/min @Thickness 0.0394 in	ISO 3795 (FMVSS 302)

Descriptive Properties	Value	Comments
Part Marking Code	>PA66-GF25<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66-GF25
Special Characteristics	Heat stabilised or stable to heat