SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON AE008XXY ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* AE008XXY is a compound based on ABS resin containing 40% Carbon Fiber. Added feature of this material ia: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.240 % | 0.240 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | 5 mm/min; ISO 527 |
| 143 MPa | 20700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D638 |
| 0.90 % | 0.90 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 25.3 GPa | 3670 ksi | 1 mm/min; ISO 527 |
| 30.06 GPa | 4360 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 200 MPa | 29000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 215 MPa | 31200 psi | ISO 178 | |
| Flexural Modulus | 23.7 GPa | 3440 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 24.67 GPa | 3578 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.17 J/cm | 5.94 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 25.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 106 °C @Thickness 3.20 mm |
223 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.0 - 6.0 ohm | 2.0 - 6.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FC 30 Low Density Polyethylene - Blown Film Extrusion
- SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific)
- PolyOne Nymax™ GF 1200 60 HS Black 22 Polyamide 66 (Nylon 66)
- Mid-Mountain Materials ARMATEX® SRS 28 Silica Fabric Coated with Silicone Rubber
- Lanxess Durethan® CI 31 F 000000 Copolyamide PA6/6I
- Lehmann & Voss LUVOCOM® 1/CF/15/TF/20/BK Polyamide 66, with carbon fiber and PTFE
- Master Bond EP38CL Adhesive Features Toughness and Durability
- A. Schulman PP 1930L-01 Polypropylene Copolymer Polypropylene
- Eurostar Staramide RFB33 PA66, 15% Glass Fiber, 15% Glass Bead Filled, Injection Molding Resin
Copyright © lookpolymers.com All Rights Reserved