LG Chemical LUPOS GP2200 ABS+GF20%, General Purpose
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled |
| Manufacturer | LG Chemical |
| Trade Name | LUPOS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOS GP2200 ABS+GF20%, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, ABS+GF20%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 2.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Yield | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 5.39 GPa @Thickness 3.20 mm |
782 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.65 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness >=1.50 mm |
140 °F @Thickness >=0.0591 in |
|
| Flammability, UL94 | HB @Thickness >=1.50 mm |
HB @Thickness >=0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 235 °C | 428 - 455 °F | Injection Molding |
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Front Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Nozzle Temperature | 230 - 245 °C | 446 - 473 °F | Injection Molding |
| Melt Temperature | 235 - 245 °C | 455 - 473 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.981 - 3.92 MPa | 142 - 569 psi | Injection Molding |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® SLX2231T PC Copolymer (Asia Pacific)
- Huntsman AVALON® 65 AB Thermoplastic Polyurethane
- Solvay Specialty Polymers Ixef® 1032 Polyarylamide (PARA), 60% Glass Fiber (Dry)
- Stir SpA POROCELL Z 660 ATS (PVC)
- Solvay MIRAPOL® WT Surfactant
- Borealis Borseal™ TD220BF Terpolymer for BOPP Film
- Dow Corning Z-1221 PHENYLMETHYLDICHLOROSILANE
- Esstech X-951-0050 BisGMA/Triethyleneglycol Dimethacrylate (50/50)
- Arkema Group Rilsan® PA 11 G BMNO MED Nylon 11
- Bhansali Engineering Abstron IM-17A ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved