Polymer Property : Melt Flow = 2.5 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	2.5 g/10 min @Load 3.80 kg, Temperature 230 °C	2.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D-1238
Plaskolite Optix® CP - 82 General Purpose Acrylic Resin OPTIX® general purpose acrylics are available in a variety of performance grades that offer varying melt flow rates, heat resistance, color/opacity and gloss levels.Information provided by Plaskoli..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Flexirene® CL 10 U Butene Copolymer Linear Low Density Polyethylene Flexirene CL 10 U is a butene copolymer linear low density polyethylene (C4-LLDPE), with antioxidants, suitable for cast extrusion of thin film with high optical properties.Main Applications: Flexi..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Polimeri Europa Greenflex® ML 40 Ethylene Vinyl Acetate Copolymer - Injection Molding Greenflex ML 40 is an ethylene vinyl acetate copolymer (EVA) for injection molding of flexible items. Items produced with Greenflex ML 40 show high elasticity and flexibility.Main Applications: Gr..
Melt Flow	2.5 g/10 min @Load 10.0 kg, Temperature 220 °C	2.5 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS..
Melt Flow	2.5 g/10 min @Load 5.00 kg, Temperature 200 °C	2.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ISO 1133
Premix Thermoplastics PRE-ELEC® PS 1328 PRE-ELEC PS 1328 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC ..
Melt Flow	2.5 g/10 min @Load 1.20 kg, Temperature 300 °C	2.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® 153 PC Nonhalogenated. 2.5 MFR. Blowmolding/extrusion. UV-stabilized.
Melt Flow	2.5 g/10 min @Load 5.00 kg, Temperature 200 °C	2.5 g/10 min @Load 11.0 lb, Temperature 392 °F	ASTM D1238
Resirene Resirene® 6420 Super High Impact Polystyrene Features:Super High ImpactEasy ProcessingLow ModulusFlexibilityFDA Rating: 21 CFR 177.1640Applications:ExtrusionDeep ThermoformingGPPS/HIPS BlendsPoint of Purchase DisplaysInformation provided by US..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F
Advanced Elastomer Systems Vistaflex® 671N Thermoplastic Rubber (discontinued **) A translucent thermoplastic elastomer with snappiness. It can be processed using injection molding or extrusion processing techniques.Key Features: Flex modulus (1% Secant) 9.0 MPa (1300 psi); Vica..
Melt Flow	2.5 g/10 min @Load 1.20 kg, Temperature 300 °C	2.5 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D 1238
SABIC Innovative Plastics Lexan® 151 PC Nonhalogenated. 2.5 MFR. Blowmolding/extrusion.This data was supplied by SABIC-IP for the Americas region.
Melt Flow	2.5 g/10 min @Load 5.00 kg, Temperature 200 °C	2.5 g/10 min @Load 11.0 lb, Temperature 392 °F	DIN 5375/ISO 1133
Ineos Nova S-5100 High Impact Compact Polystyrene (discontinued **) All mechanical properties measured under standard conditions 50% RH and 23°C.Information provided by NOVA Chemicals.INEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture betwee..
Melt Flow	2.5 g/10 min	2.5 g/10 min	DIN 53735/ISO 1133
Ineos Nova S-7600MG Compact Polystyrene Microgranulates (discontinued **) High impact polystyrene Microgranulates, having a diameter of 0.8 -1.0 mm, especially useful for compounding and extrusion applications. Due to the very high viscosity and the absence of weakener, ..
Melt Flow	2.5 g/10 min	2.5 g/10 min	ASTM D1238
LyondellBasell Petrothene® NA420127 Low Density Polyethylene (discontinued **) ApplicationsPETROTHENE NA 420 is a LDPE/EVA copolymer resin for high impact and clarity packaging film. This resin exhibits excellent processability over a broad range of extrusion conditions. Wel..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
DuPont Performance Polymers Delrin® 100P BK602 Acetal Homopolymer (Unverified Data**) Delrin® 100P is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin® 100P provides maximum toughness in the product line without modification. Delrin® 100P has improved pro..
Melt Flow	2.5 - 4.5 g/10 min @Load 2.16 kg, Temperature 190 Â°C	2.5 - 4.5 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ISO 1133
FKuR Kunststoff Bio-FlexÂ® F 6510 Compostable PLA Blend The BIO-FLEXÂ® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEXÂ® does not contain any sta..
Melt Flow	2.5 g/10 min	2.5 g/10 min	ASTM D1238
Hyosung Topilene J340F PP J340F Film Grade Impact CopolymerApplications: Retort CPPCharacteristics:ProcessabilityHigh impactInformation provided by Hyosung Corporation
Melt Flow	2.5 g/10 min	2.5 g/10 min	Condition G
Ineos Nova 5404 High Impact Polystyrene High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	2.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238
Ineos N02G-00 Polypropylene Impact Copolymer Grade N02G-00 is a low melt flow rate, high-impact copolymer polypropylene for sheet extrusion and thick wall injection molding applications. It offers a superior balance of stiffness and impact str..
Melt Flow	2.5 g/10 min @Load 3.80 kg, Temperature 230 Â°C	2.5 g/10 min @Load 8.38 lb, Temperature 446 Â°F	ASTM Data
Styron Magnumâ„¢ 9030 ABS, High Gloss MAGNUMÂ® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM-D1238
Westlake EMAC® SP2404 18.5% EMA Copolymer Westlake EMACï¿½ SP2404 is a 18.5% EMA copolymer designed for blown film, tie-layer, coextrusions, and blending where flexibility and strength are important. SP2404 provides excellent elasticity ..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
ExxonMobil LDPE LD 313.NF Low Density Polyethylene Resin Product Description: LD 313.NF is a 3 % vinyl acetate copolymer. The vinyl acetate content of this resin provides good heat sealing and good cold temperature toughness when compared to LDPE homopoly..
Melt Flow	2.5 g/10 min	2.5 g/10 min	ASTM D1238
Dow DOWLEX™ 2036G Linear Low Density Polyethylene Improved thermal stability for high stiffness film applications Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 235 °C	2.5 g/10 min @Load 4.76 lb, Temperature 455 °F
Arkema Group Rilsan® AESN TL Nylon 12, Flexible Tubing Grade (Conditioned) Designation ISO 1874-PA12,EHL,22-010Rigid grade for tubes extrusion. Available colors: black and natural. Light and heat stabilized.High impact strength. Good chemical resistance. Very good ability ..
Melt Flow	2.5 g/10 min @Load 5.00 kg, Temperature 200 °C	2.5 g/10 min @Load 11.0 lb, Temperature 392 °F
BASF Polystyrol® 165 H Polystyrene (Europe) High molecular grades, often blended with high-impact extrusion grades (e.g. for dairy products).Data was collected by ISO methods and provided by BASF.
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
BLUESTAR BS025 Acetal Copolymer Information provided by Polymer Technology and Services, LLC (PTS).
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Azoty Tarnow™ TARNOFORM 200 POM This material is a standard extrusion grade, also could be used for injection molding of low shape complexity details.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A.
Melt Flow	2.5 g/10 min @Load 3.80 kg, Temperature 230 °C	2.5 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D-1238
Plaskolite West Optix® CP - 82 General Purpose Acrylic Resin Generally unaffected by alkalis, hydrocarbons, non-oxidizing acids, and salt water. Transparent, translucent, opaque, and custom colors in various grades of melt flow rate and heat resistance are av..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 280 °C	2.5 g/10 min @Load 4.76 lb, Temperature 536 °F	cm³/10min; ISO 1133
DuPont Performance Polymers Rynite® 545 NC010 Polyethylene Terephthalate (PET) (Unverified Data**) 45% Glass Reinforced Polyethylene Terephthalate Rynite 545 NC010 is a 45% glass reinforced modified polyethylene terephthalate with greater strength and stiffness excellent dimensional stability and..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
DuPont Nucrel® 0903B Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film (discontinued **) 9 wt% Methacrylic Acid.Nucrel® 0903B is an ethylene-methacrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion processes designed to process polyethylene re..
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 230 °C	2.5 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Polyram RamOfin PPH308G8 Polypropylene, 40% Glass Fiber 40% glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.