LG Chemical LUPOS GP2100 ABS+GF10%, General Purpose

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUPOS
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOS GP2100 ABS+GF10%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, ABS+GF10%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-56-9, 9003-54-7 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0040 in/in

@Thickness 0.126 in
ASTM D955
Melt Flow 4.2 g/10 min

@Load 3.80 kg,
Temperature 230 °C
4.2 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114
114
ASTM D785
Tensile Strength, Yield 64.7 MPa

@Thickness 3.20 mm
9390 psi

@Thickness 0.126 in
50mm/min; ASTM D638
Elongation at Break 5.0 %

@Thickness 3.20 mm
5.0 %

@Thickness 0.126 in
50mm/min; ASTM D638
Flexural Yield Strength 108 MPa

@Thickness 3.20 mm
15600 psi

@Thickness 0.126 in
10mm/min; ASTM D790
Flexural Modulus 3.73 GPa

@Thickness 3.20 mm
540 ksi

@Thickness 0.126 in
10mm/min; ASTM D790
Izod Impact, Notched 0.981 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.84 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C

@Thickness 6.40 mm
207 °F

@Thickness 0.252 in
Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
140 °F

@Thickness >=0.0591 in
Flammability, UL94 HB

@Thickness >=1.50 mm
HB

@Thickness >=0.0591 in
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 235 °C
428 - 455 °F
Injection Molding
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Front Barrel Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Nozzle Temperature 230 - 245 °C
446 - 473 °F
Injection Molding
Melt Temperature 235 - 245 °C
455 - 473 °F
Injection Molding
Mold Temperature 50.0 - 80.0 °C
122 - 176 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 60 rpm
40 - 60 rpm
Injection Molding