LG Chemical LUPOL HF-3308 High Flow Polypropylene, 30% Mineral Fillers
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL HF-3308 High Flow Polypropylene, 30% Mineral Fillers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner, mud guard, door trim, garnishElectrical and Electronic: Tail lamp housing, air conditioner housing, fan, socket, washing machine partsIndustrial Parts and Household Appliance:Propeller fan, pulley, container, pump container, pump casing, handle and switch cover of electric jar, fan shroud/supportInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 39.0 MPa | 5660 psi | ASTM D790 |
| Flexural Modulus | 2.75 GPa | 399 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour | |
| Injection Pressure | 29.4 - 118 MPa | 4260 - 17100 psi | First |
| 78.45 - 98.07 MPa | 11380 - 14220 psi | Second | |
| Back Pressure | 0.490 - 3.92 MPa | 71.1 - 569 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® PC1800 PC (Asia Pacific)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Sulfur Cure
- LyondellBasell Lupolen® 1800 S LDPE, Injection Molding Grade
- SABIC Innovative Plastics Valox® V9260CS PET (Asia Pacific)
- Shin-Etsu Silicones KBE-3803A Fluid
- Dyna-Purge® SF Purging Compound
- Silikony Polskie Polsil OM 2000 Methyl Silicone Fluid
- Plenco 7591 Phenolic, Briquette, Injection Molded
- Dow Corning LSPRD12 SILICONE MASTERBATCH RED
- LNP ULTEM® SMU5831 Polyetherimide, 30% CarbonGlassMineral Reinforced (discontinued **)
Copyright © lookpolymers.com All Rights Reserved