- Schwartz Technical Plastics LAMINEX® 2010 Cotton Fabric, Phenolic Resin Impregnated, Fine
Schwartz Technical Plastics LAMINEX® 2010 Cotton Fabric, Phenolic Resin Impregnated, Fine
| Category | Polymer , Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMINEX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMINEX® 2010 Cotton Fabric, Phenolic Resin Impregnated, Fine.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: slippers, inserts for coupling boxes, rollneck bearingsInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO R 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO-DIS 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | DIN 53457 |
| Flexural Strength | 100 - 130 MPa | 14500 - 18900 psi | DIN 54352 |
| Compressive Strength | 170 MPa | 24700 psi | ISO 604 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | DIN 53453 |
| Izod Impact Resistance | 3.00 J/cm² | 14.3 ft-lb/in² | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.020 | 0.020 | With lubrication |
| Coefficient of Friction, Dynamic | 0.020 | 0.020 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 - 100 °C |
16.7 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 150 °C | 302 °F | Intermittent |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | DIN 53482 |
| Dielectric Constant | 5.0 | 5.0 | DIN 53483 |
| Dielectric Loss Index | 0.30 | 0.30 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA1 | DIN 53480 |
| Moisture Absorption at Equilibrium | 100 mg | DIN 53472 |
Users viewing this material also viewed the following:
- Polimeri Europa Extir® LN 3000 Expandable Polystyrene
- Ravago Manufacturing Americas Hylon® N1233HL BK Nylon 6/6
- Victrex® PEEK -HT™ 22CA30 PolyEtherKetone, 30% Carbon Fibre Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP BX02715 SAN
- MetalTek MTEK 65 UNS C90700 Gear Bronze
- Struktol TPW 709 Processing Additive
- Sumitomo Chemical ESPOLEX® 822 Thermoplastic Elastomer
- A. Schulman POLYFORT™ PX 1042
- A. Schulman POLYFORT™ FPP 2067HU UV Stabilized, High Heat Resistant Impact Polypropylene
- Saint-Gobain Chemfab® 14 High-Performance PTFE-Coated Glass
Copyright © lookpolymers.com All Rights Reserved