LG Chemical LUPOL GP3156F Flame Retardant PP

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOL GP3156F Flame Retardant PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, FR PP, General Purpose, Flame RetardantApplication: Electrical & Electronic, Automotive PartsCAS: 9003-07-0, 84852-53-9, 14807-96-6 and 1309-64-4Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0090 - 0.013 cm/cm

@Thickness 3.20 mm
 0.0090 - 0.013 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 6.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 6.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 27.5 MPa

@Thickness 3.20 mm
 3980 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 38.2 MPa

@Thickness 6.40 mm
 5550 psi

@Thickness 0.252 in
 10mm/min; ASTM D790
Flexural Modulus 1.77 GPa

@Thickness 6.40 mm
 256 ksi

@Thickness 0.252 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 0.490 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 >= 0.918 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 135 °C

@Thickness 3.20 mm
 275 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
UL RTI, Electrical 125 °C

@Thickness >=0.750 mm
 257 °F

@Thickness >=0.0295 in
125 °C

@Thickness >=1.50 mm
 257 °F

@Thickness >=0.0591 in
125 °C

@Thickness >=2.00 mm
 257 °F

@Thickness >=0.0787 in
125 °C

@Thickness >=3.00 mm
 257 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 120 °C

@Thickness >=0.750 mm
 248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=2.00 mm
 248 °F

@Thickness >=0.0787 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 120 °C

@Thickness >=0.750 mm
 248 °F

@Thickness >=0.0295 in
120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=2.00 mm
 248 °F

@Thickness >=0.0787 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
Flammability, UL94 V-0

@Thickness >=0.750 mm
 V-0

@Thickness >=0.0295 in
V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=2.00 mm
 V-0

@Thickness >=0.0787 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
5VB

@Thickness >=2.00 mm
 5VB

@Thickness >=0.0787 in
5VB

@Thickness >=3.00 mm
 5VB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=0.750 mm
 15 - 30 sec

@Thickness >=0.0295 in
15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=2.00 mm
 15 - 30 sec

@Thickness >=0.0787 in
30 - 60 sec

@Thickness >=3.00 mm
 30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 2.00 mm
 >= 120 arcs

@Thickness 0.0787 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Middle Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Front Barrel Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Nozzle Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding
Users viewing this material also viewed the following: